UHMWPE marine fender pads possess outstanding abrasion resistance, capable of withstanding the friction generated during vessel berthing and unberthing. By reducing direct contact between vessels and dock structures,
UHMW-PE fender pads effectively minimize the risks of wear and damage, extending the lifespan of dock structures.
- Outstanding Characteristics
| Light Weight | Ozone Resistant | High Impact Strength | 100% Recyclable |
| Abrasion Resistance | Hygienic and Non-toxic | Low Co-efficient of Friction | Chemical Resistance |
| Shock and Noise Absorption | No Moisture Absorption | Excellent Self-lubrication | Anti-aging |
| Temperature Resistant(-100°C to +80°C) | |||
| Excellent UV Stability – Highly Suited to the Harsh Climate | |||
| Can Be Pre-drilled for Easy Installation and Chamfered to Avoid Rough Machining | |||
To give you a better idea of the capabilities of our fender frontal pads, we have included some detailed technical specifications below:
| Property | Test Method | Raw Material | Unit |
| Molecular Weight | 3~9 million | g/mol | |
| Density | ISO 1183-1:2012/DIN53479 | 0.92-0.98 | g/cm³ |
| Compression Strength | ISO 604:2002 | ≥32 | Mpa |
| Tensile Strength | ISO 527-2:2012 | ≥22 | Mpa |
| Elongation at Break | ISO 527-2:2012 | ≥280 | % |
| Dynamic Friction Coefficient | ASTM D 1894/GB10006-88 | ≤0.18 | |
| Notched Impact Strength(Charpy) | ISO 179-1:2010/GB/T 1043.1-2008 | ≥100 | kJ/m² |
| Vicat Softing Point | ISO 306:2004 | ≥80 | ℃ |
| Shore Hardness – D | ISO 868：2003 | 61-66 | D |
Values are averages.ASTM test methods are under current standards.
Size: The manufacturing process does not limit the cross-sections and plate dimensions.
Thickness: 6-300mm
Maximum size: 6000*2000mm
The standard color is black.
Other colors such as blue, green,yellow, white or red is also avaiable upon request.